The effect of magnetic field on copper in various corrosive medium

L. Y. Ang, N. K. Othman, Azman Jalar @ Jalil, I. Ismail

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The effect of applied magnetic field on the corrosion behaviour of copper within various corrosive medium is investigated. The copper coupon is immersed in 0.5 M HCl, 0.5 M NaCl and 0.5 M NaOH with or without applying up to 40 mT magnetic fields for 24 hours. The weight loss of copper coupon in HCl increased up to 96.56% with applied magnetic fields. However, in NaOH medium, only 33.33% more weight loss was observed and no difference were observed for coupons in NaCl when magnetic field is applied. This observation indicates that corrosion behaviour in HCl and NaOH is controlled by mass transport that can be influenced by the induced magneto hydrodynamics effect when magnetic field is applied. There was no change in weight loss of copper in NaCl when magnetic field is applied because the corrosion mechanism of copper in NaCl is governed by electron charge transfer.

Original languageEnglish
Title of host publication2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium
EditorsZahari Ibrahim, Haja Maideen Kader Maideen, Nazlina Ibrahim, Nurul Huda Abd Karim, Taufik Yusof, Fatimah Abdul Razak, Nurulkamal Maseran, Rozida Mohd Khalid, Noor Baa'yah Ibrahim, Hasidah Mohd. Sidek, Mohd Salmi Md Noorani, Norbert Simon
PublisherAmerican Institute of Physics Inc.
Pages26-29
Number of pages4
ISBN (Electronic)9780735412507
DOIs
Publication statusPublished - 1 Jan 2014
Event2014 Postgraduate Colloquium of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology, UKM FST 2014 - Selangor, Malaysia
Duration: 9 Apr 201411 Apr 2014

Publication series

NameAIP Conference Proceedings
Volume1614
ISSN (Print)0094-243X
ISSN (Electronic)1551-7616

Other

Other2014 Postgraduate Colloquium of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology, UKM FST 2014
CountryMalaysia
CitySelangor
Period9/4/1411/4/14

Fingerprint

copper
magnetic fields
corrosion
hydrodynamics
charge transfer
electrons

Keywords

  • Copper
  • Corrosion
  • Magnetic field

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Ang, L. Y., Othman, N. K., Jalar @ Jalil, A., & Ismail, I. (2014). The effect of magnetic field on copper in various corrosive medium. In Z. Ibrahim, H. M. K. Maideen, N. Ibrahim, N. H. A. Karim, T. Yusof, F. A. Razak, N. Maseran, R. M. Khalid, N. B. Ibrahim, H. M. Sidek, M. S. M. Noorani, ... N. Simon (Eds.), 2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium (pp. 26-29). (AIP Conference Proceedings; Vol. 1614). American Institute of Physics Inc.. https://doi.org/10.1063/1.4895164

The effect of magnetic field on copper in various corrosive medium. / Ang, L. Y.; Othman, N. K.; Jalar @ Jalil, Azman; Ismail, I.

2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium. ed. / Zahari Ibrahim; Haja Maideen Kader Maideen; Nazlina Ibrahim; Nurul Huda Abd Karim; Taufik Yusof; Fatimah Abdul Razak; Nurulkamal Maseran; Rozida Mohd Khalid; Noor Baa'yah Ibrahim; Hasidah Mohd. Sidek; Mohd Salmi Md Noorani; Norbert Simon. American Institute of Physics Inc., 2014. p. 26-29 (AIP Conference Proceedings; Vol. 1614).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Ang, LY, Othman, NK, Jalar @ Jalil, A & Ismail, I 2014, The effect of magnetic field on copper in various corrosive medium. in Z Ibrahim, HMK Maideen, N Ibrahim, NHA Karim, T Yusof, FA Razak, N Maseran, RM Khalid, NB Ibrahim, HM Sidek, MSM Noorani & N Simon (eds), 2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium. AIP Conference Proceedings, vol. 1614, American Institute of Physics Inc., pp. 26-29, 2014 Postgraduate Colloquium of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology, UKM FST 2014, Selangor, Malaysia, 9/4/14. https://doi.org/10.1063/1.4895164
Ang LY, Othman NK, Jalar @ Jalil A, Ismail I. The effect of magnetic field on copper in various corrosive medium. In Ibrahim Z, Maideen HMK, Ibrahim N, Karim NHA, Yusof T, Razak FA, Maseran N, Khalid RM, Ibrahim NB, Sidek HM, Noorani MSM, Simon N, editors, 2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium. American Institute of Physics Inc. 2014. p. 26-29. (AIP Conference Proceedings). https://doi.org/10.1063/1.4895164
Ang, L. Y. ; Othman, N. K. ; Jalar @ Jalil, Azman ; Ismail, I. / The effect of magnetic field on copper in various corrosive medium. 2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium. editor / Zahari Ibrahim ; Haja Maideen Kader Maideen ; Nazlina Ibrahim ; Nurul Huda Abd Karim ; Taufik Yusof ; Fatimah Abdul Razak ; Nurulkamal Maseran ; Rozida Mohd Khalid ; Noor Baa'yah Ibrahim ; Hasidah Mohd. Sidek ; Mohd Salmi Md Noorani ; Norbert Simon. American Institute of Physics Inc., 2014. pp. 26-29 (AIP Conference Proceedings).
@inproceedings{4c725aef8f01442b9917350001e22f58,
title = "The effect of magnetic field on copper in various corrosive medium",
abstract = "The effect of applied magnetic field on the corrosion behaviour of copper within various corrosive medium is investigated. The copper coupon is immersed in 0.5 M HCl, 0.5 M NaCl and 0.5 M NaOH with or without applying up to 40 mT magnetic fields for 24 hours. The weight loss of copper coupon in HCl increased up to 96.56{\%} with applied magnetic fields. However, in NaOH medium, only 33.33{\%} more weight loss was observed and no difference were observed for coupons in NaCl when magnetic field is applied. This observation indicates that corrosion behaviour in HCl and NaOH is controlled by mass transport that can be influenced by the induced magneto hydrodynamics effect when magnetic field is applied. There was no change in weight loss of copper in NaCl when magnetic field is applied because the corrosion mechanism of copper in NaCl is governed by electron charge transfer.",
keywords = "Copper, Corrosion, Magnetic field",
author = "Ang, {L. Y.} and Othman, {N. K.} and {Jalar @ Jalil}, Azman and I. Ismail",
year = "2014",
month = "1",
day = "1",
doi = "10.1063/1.4895164",
language = "English",
series = "AIP Conference Proceedings",
publisher = "American Institute of Physics Inc.",
pages = "26--29",
editor = "Zahari Ibrahim and Maideen, {Haja Maideen Kader} and Nazlina Ibrahim and Karim, {Nurul Huda Abd} and Taufik Yusof and Razak, {Fatimah Abdul} and Nurulkamal Maseran and Khalid, {Rozida Mohd} and Ibrahim, {Noor Baa'yah} and Sidek, {Hasidah Mohd.} and Noorani, {Mohd Salmi Md} and Norbert Simon",
booktitle = "2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium",

}

TY - GEN

T1 - The effect of magnetic field on copper in various corrosive medium

AU - Ang, L. Y.

AU - Othman, N. K.

AU - Jalar @ Jalil, Azman

AU - Ismail, I.

PY - 2014/1/1

Y1 - 2014/1/1

N2 - The effect of applied magnetic field on the corrosion behaviour of copper within various corrosive medium is investigated. The copper coupon is immersed in 0.5 M HCl, 0.5 M NaCl and 0.5 M NaOH with or without applying up to 40 mT magnetic fields for 24 hours. The weight loss of copper coupon in HCl increased up to 96.56% with applied magnetic fields. However, in NaOH medium, only 33.33% more weight loss was observed and no difference were observed for coupons in NaCl when magnetic field is applied. This observation indicates that corrosion behaviour in HCl and NaOH is controlled by mass transport that can be influenced by the induced magneto hydrodynamics effect when magnetic field is applied. There was no change in weight loss of copper in NaCl when magnetic field is applied because the corrosion mechanism of copper in NaCl is governed by electron charge transfer.

AB - The effect of applied magnetic field on the corrosion behaviour of copper within various corrosive medium is investigated. The copper coupon is immersed in 0.5 M HCl, 0.5 M NaCl and 0.5 M NaOH with or without applying up to 40 mT magnetic fields for 24 hours. The weight loss of copper coupon in HCl increased up to 96.56% with applied magnetic fields. However, in NaOH medium, only 33.33% more weight loss was observed and no difference were observed for coupons in NaCl when magnetic field is applied. This observation indicates that corrosion behaviour in HCl and NaOH is controlled by mass transport that can be influenced by the induced magneto hydrodynamics effect when magnetic field is applied. There was no change in weight loss of copper in NaCl when magnetic field is applied because the corrosion mechanism of copper in NaCl is governed by electron charge transfer.

KW - Copper

KW - Corrosion

KW - Magnetic field

UR - http://www.scopus.com/inward/record.url?scp=85063845668&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85063845668&partnerID=8YFLogxK

U2 - 10.1063/1.4895164

DO - 10.1063/1.4895164

M3 - Conference contribution

AN - SCOPUS:85063845668

T3 - AIP Conference Proceedings

SP - 26

EP - 29

BT - 2014 UKM FST Postgraduate Colloquium - Proceedings of the Universiti Kebangsaan Malaysia, Faculty of Science and Technology 2014 Postgraduate Colloquium

A2 - Ibrahim, Zahari

A2 - Maideen, Haja Maideen Kader

A2 - Ibrahim, Nazlina

A2 - Karim, Nurul Huda Abd

A2 - Yusof, Taufik

A2 - Razak, Fatimah Abdul

A2 - Maseran, Nurulkamal

A2 - Khalid, Rozida Mohd

A2 - Ibrahim, Noor Baa'yah

A2 - Sidek, Hasidah Mohd.

A2 - Noorani, Mohd Salmi Md

A2 - Simon, Norbert

PB - American Institute of Physics Inc.

ER -