Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills

M. Suhaily, Che Hassan Che Haron, Jaharah A Ghani, H. Azmi, M. A. Afifah, M. K.Nor Khairusshima

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

In this research study, it presents the influences of drilling parameters on the delamination factor during the drilling of woven kenaf fiber reinforced epoxy composite laminates when using the carbide drill bits. The purpose of this study is to investigate the influence of drilling parameters such as cutting speed, feed rate and drill sizes on the delamination produced when drilling woven kenaf reinforced epoxy composite using the non-coated carbide drill bits. The damage generated on the woven kenaf reinforced epoxy composite laminates were observed both at the entrance and exit surface during the drilling operation. The experiments were conducted according to the Box Behnken experimental designs. The results indicated that the drill diameter has a significant influence on the delamination when drilling the woven kenaf fiber reinforced epoxy composites.

Original languageEnglish
Title of host publication2018 6th International Conference on Nano and Materials Science, ICNMS 2018
PublisherAmerican Institute of Physics Inc.
Volume1957
ISBN (Electronic)9780735416581
DOIs
Publication statusPublished - 19 Apr 2018
Event2018 6th International Conference on Nano and Materials Science, ICNMS 2018 - Lakeland, United States
Duration: 15 Jan 201817 Jan 2018

Other

Other2018 6th International Conference on Nano and Materials Science, ICNMS 2018
CountryUnited States
CityLakeland
Period15/1/1817/1/18

Fingerprint

drilling
carbides
composite materials
fibers
drill bits
laminates
entrances
boxes
damage

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Suhaily, M., Che Haron, C. H., A Ghani, J., Azmi, H., Afifah, M. A., & Khairusshima, M. K. N. (2018). Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills. In 2018 6th International Conference on Nano and Materials Science, ICNMS 2018 (Vol. 1957). [0500041] American Institute of Physics Inc.. https://doi.org/10.1063/1.5034334

Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills. / Suhaily, M.; Che Haron, Che Hassan; A Ghani, Jaharah; Azmi, H.; Afifah, M. A.; Khairusshima, M. K.Nor.

2018 6th International Conference on Nano and Materials Science, ICNMS 2018. Vol. 1957 American Institute of Physics Inc., 2018. 0500041.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Suhaily, M, Che Haron, CH, A Ghani, J, Azmi, H, Afifah, MA & Khairusshima, MKN 2018, Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills. in 2018 6th International Conference on Nano and Materials Science, ICNMS 2018. vol. 1957, 0500041, American Institute of Physics Inc., 2018 6th International Conference on Nano and Materials Science, ICNMS 2018, Lakeland, United States, 15/1/18. https://doi.org/10.1063/1.5034334
Suhaily M, Che Haron CH, A Ghani J, Azmi H, Afifah MA, Khairusshima MKN. Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills. In 2018 6th International Conference on Nano and Materials Science, ICNMS 2018. Vol. 1957. American Institute of Physics Inc. 2018. 0500041 https://doi.org/10.1063/1.5034334
Suhaily, M. ; Che Haron, Che Hassan ; A Ghani, Jaharah ; Azmi, H. ; Afifah, M. A. ; Khairusshima, M. K.Nor. / Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills. 2018 6th International Conference on Nano and Materials Science, ICNMS 2018. Vol. 1957 American Institute of Physics Inc., 2018.
@inproceedings{be0d0f6bb7c64f5c9f1d7ca57fe69b26,
title = "Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills",
abstract = "In this research study, it presents the influences of drilling parameters on the delamination factor during the drilling of woven kenaf fiber reinforced epoxy composite laminates when using the carbide drill bits. The purpose of this study is to investigate the influence of drilling parameters such as cutting speed, feed rate and drill sizes on the delamination produced when drilling woven kenaf reinforced epoxy composite using the non-coated carbide drill bits. The damage generated on the woven kenaf reinforced epoxy composite laminates were observed both at the entrance and exit surface during the drilling operation. The experiments were conducted according to the Box Behnken experimental designs. The results indicated that the drill diameter has a significant influence on the delamination when drilling the woven kenaf fiber reinforced epoxy composites.",
author = "M. Suhaily and {Che Haron}, {Che Hassan} and {A Ghani}, Jaharah and H. Azmi and Afifah, {M. A.} and Khairusshima, {M. K.Nor}",
year = "2018",
month = "4",
day = "19",
doi = "10.1063/1.5034334",
language = "English",
volume = "1957",
booktitle = "2018 6th International Conference on Nano and Materials Science, ICNMS 2018",
publisher = "American Institute of Physics Inc.",

}

TY - GEN

T1 - Study on drilling induced delamination of woven kenaf fiber reinforced epoxy composite using carbide drills

AU - Suhaily, M.

AU - Che Haron, Che Hassan

AU - A Ghani, Jaharah

AU - Azmi, H.

AU - Afifah, M. A.

AU - Khairusshima, M. K.Nor

PY - 2018/4/19

Y1 - 2018/4/19

N2 - In this research study, it presents the influences of drilling parameters on the delamination factor during the drilling of woven kenaf fiber reinforced epoxy composite laminates when using the carbide drill bits. The purpose of this study is to investigate the influence of drilling parameters such as cutting speed, feed rate and drill sizes on the delamination produced when drilling woven kenaf reinforced epoxy composite using the non-coated carbide drill bits. The damage generated on the woven kenaf reinforced epoxy composite laminates were observed both at the entrance and exit surface during the drilling operation. The experiments were conducted according to the Box Behnken experimental designs. The results indicated that the drill diameter has a significant influence on the delamination when drilling the woven kenaf fiber reinforced epoxy composites.

AB - In this research study, it presents the influences of drilling parameters on the delamination factor during the drilling of woven kenaf fiber reinforced epoxy composite laminates when using the carbide drill bits. The purpose of this study is to investigate the influence of drilling parameters such as cutting speed, feed rate and drill sizes on the delamination produced when drilling woven kenaf reinforced epoxy composite using the non-coated carbide drill bits. The damage generated on the woven kenaf reinforced epoxy composite laminates were observed both at the entrance and exit surface during the drilling operation. The experiments were conducted according to the Box Behnken experimental designs. The results indicated that the drill diameter has a significant influence on the delamination when drilling the woven kenaf fiber reinforced epoxy composites.

UR - http://www.scopus.com/inward/record.url?scp=85046119949&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85046119949&partnerID=8YFLogxK

U2 - 10.1063/1.5034334

DO - 10.1063/1.5034334

M3 - Conference contribution

VL - 1957

BT - 2018 6th International Conference on Nano and Materials Science, ICNMS 2018

PB - American Institute of Physics Inc.

ER -