Solvent debinding process for ZK60 magnesium alloy mim compact

Mohd Ruzi Harun, Norhamidi Muhamad, Abu Bakar Sulong, Nor Hafiez Mohamad Nor, Khairur Rijal Jamaludin, Mohd Halimirwan Ibrahim

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

The influence of the leaching temperatures on the solvent debinding process of ZK60 magnesium alloy compact has been investigated. In this experiment, the soluble binder, palm stearin molecules were extracted out from the compact parts by immersing the compact parts in an n-heptanes solution. The solvent debinding rate was then investigated under the conditions of different leaching temperatures. The weight loss percentages of palm stearin were calculated and the pore structure evolution was analyzed by scanning electron micrograph. Results show that a complete diffusion of the palm stearin molecules out of the compact part best at 60° within 4 hours of extraction time.

Original languageEnglish
Pages (from-to)159-168
Number of pages10
JournalJurnal Teknologi (Sciences and Engineering)
Volume59
Issue numberSUPPL.2
Publication statusPublished - 2012

Fingerprint

Magnesium alloys
Leaching
Molecules
Heptane
Pore structure
Binders
Scanning
Temperature
Electrons
Experiments

Keywords

  • Debinding rate
  • Magnesium alloy
  • Metal injection moulding
  • Palm stearin

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Harun, M. R., Muhamad, N., Sulong, A. B., Mohamad Nor, N. H., Jamaludin, K. R., & Ibrahim, M. H. (2012). Solvent debinding process for ZK60 magnesium alloy mim compact. Jurnal Teknologi (Sciences and Engineering), 59(SUPPL.2), 159-168.

Solvent debinding process for ZK60 magnesium alloy mim compact. / Harun, Mohd Ruzi; Muhamad, Norhamidi; Sulong, Abu Bakar; Mohamad Nor, Nor Hafiez; Jamaludin, Khairur Rijal; Ibrahim, Mohd Halimirwan.

In: Jurnal Teknologi (Sciences and Engineering), Vol. 59, No. SUPPL.2, 2012, p. 159-168.

Research output: Contribution to journalArticle

Harun, MR, Muhamad, N, Sulong, AB, Mohamad Nor, NH, Jamaludin, KR & Ibrahim, MH 2012, 'Solvent debinding process for ZK60 magnesium alloy mim compact', Jurnal Teknologi (Sciences and Engineering), vol. 59, no. SUPPL.2, pp. 159-168.
Harun, Mohd Ruzi ; Muhamad, Norhamidi ; Sulong, Abu Bakar ; Mohamad Nor, Nor Hafiez ; Jamaludin, Khairur Rijal ; Ibrahim, Mohd Halimirwan. / Solvent debinding process for ZK60 magnesium alloy mim compact. In: Jurnal Teknologi (Sciences and Engineering). 2012 ; Vol. 59, No. SUPPL.2. pp. 159-168.
@article{fef6cc13ee7940d3aab5607fb97c2c64,
title = "Solvent debinding process for ZK60 magnesium alloy mim compact",
abstract = "The influence of the leaching temperatures on the solvent debinding process of ZK60 magnesium alloy compact has been investigated. In this experiment, the soluble binder, palm stearin molecules were extracted out from the compact parts by immersing the compact parts in an n-heptanes solution. The solvent debinding rate was then investigated under the conditions of different leaching temperatures. The weight loss percentages of palm stearin were calculated and the pore structure evolution was analyzed by scanning electron micrograph. Results show that a complete diffusion of the palm stearin molecules out of the compact part best at 60° within 4 hours of extraction time.",
keywords = "Debinding rate, Magnesium alloy, Metal injection moulding, Palm stearin",
author = "Harun, {Mohd Ruzi} and Norhamidi Muhamad and Sulong, {Abu Bakar} and {Mohamad Nor}, {Nor Hafiez} and Jamaludin, {Khairur Rijal} and Ibrahim, {Mohd Halimirwan}",
year = "2012",
language = "English",
volume = "59",
pages = "159--168",
journal = "Jurnal Teknologi",
issn = "0127-9696",
publisher = "Penerbit Universiti Teknologi Malaysia",
number = "SUPPL.2",

}

TY - JOUR

T1 - Solvent debinding process for ZK60 magnesium alloy mim compact

AU - Harun, Mohd Ruzi

AU - Muhamad, Norhamidi

AU - Sulong, Abu Bakar

AU - Mohamad Nor, Nor Hafiez

AU - Jamaludin, Khairur Rijal

AU - Ibrahim, Mohd Halimirwan

PY - 2012

Y1 - 2012

N2 - The influence of the leaching temperatures on the solvent debinding process of ZK60 magnesium alloy compact has been investigated. In this experiment, the soluble binder, palm stearin molecules were extracted out from the compact parts by immersing the compact parts in an n-heptanes solution. The solvent debinding rate was then investigated under the conditions of different leaching temperatures. The weight loss percentages of palm stearin were calculated and the pore structure evolution was analyzed by scanning electron micrograph. Results show that a complete diffusion of the palm stearin molecules out of the compact part best at 60° within 4 hours of extraction time.

AB - The influence of the leaching temperatures on the solvent debinding process of ZK60 magnesium alloy compact has been investigated. In this experiment, the soluble binder, palm stearin molecules were extracted out from the compact parts by immersing the compact parts in an n-heptanes solution. The solvent debinding rate was then investigated under the conditions of different leaching temperatures. The weight loss percentages of palm stearin were calculated and the pore structure evolution was analyzed by scanning electron micrograph. Results show that a complete diffusion of the palm stearin molecules out of the compact part best at 60° within 4 hours of extraction time.

KW - Debinding rate

KW - Magnesium alloy

KW - Metal injection moulding

KW - Palm stearin

UR - http://www.scopus.com/inward/record.url?scp=84872744651&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84872744651&partnerID=8YFLogxK

M3 - Article

VL - 59

SP - 159

EP - 168

JO - Jurnal Teknologi

JF - Jurnal Teknologi

SN - 0127-9696

IS - SUPPL.2

ER -