Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition

E. Taer, Mohamad Deraman, R. Taslim, Iwantono

Research output: Chapter in Book/Report/Conference proceedingConference contribution

16 Citations (Scopus)

Abstract

Binderless activated carbon monolith (ACM) was prepared from pre-carbonized rubber wood sawdust (RWSD). The effect of the carbonization temperature (400, 500, 600, 700, 800 dan 900 °C) on porosity characteristic of the ACM have been studied. The optimum carbonization temperature for obtaining ACM with high surface area of 600 °C with CO2 activation at 800 °C for one hour. At this condition, the surface area as high as 733 m2 g-1 could be successfully obtained. By improved the activation temperature at 900 °C for 2.5 h, it was found that the surface area of 860 m2 g-1. For this condition, the ACM exhibit the specific capacitance of 90 F g-1. In addition the termogravimertic (TG)-differential termografimertic (DTG) and field emission scanning electron microscope (FESEM) measurement were also performed on the ACMs and the result has been studied. Finally, it was conclude that the high surface area of ACM from RWSD could be produced by proper selections of carbonization and activation condition.

Original languageEnglish
Title of host publicationAIP Conference Proceedings
Pages33-37
Number of pages5
Volume1554
DOIs
Publication statusPublished - 2013
EventPadjadjaran International Physics Symposium 2013: Contribution of Physics on Environmental and Energy Conservations, PIPS 2013 - Jatinangor, Bandung
Duration: 7 May 20139 May 2013

Other

OtherPadjadjaran International Physics Symposium 2013: Contribution of Physics on Environmental and Energy Conservations, PIPS 2013
CityJatinangor, Bandung
Period7/5/139/5/13

Fingerprint

carbonization
activated carbon
rubber
activation
preparation
temperature
field emission
electron microscopes
capacitance
porosity
scanning

Keywords

  • Activated carbon
  • Specific capacitance
  • Supercapacitor

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition. / Taer, E.; Deraman, Mohamad; Taslim, R.; Iwantono.

AIP Conference Proceedings. Vol. 1554 2013. p. 33-37.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Taer, E, Deraman, M, Taslim, R & Iwantono 2013, Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition. in AIP Conference Proceedings. vol. 1554, pp. 33-37, Padjadjaran International Physics Symposium 2013: Contribution of Physics on Environmental and Energy Conservations, PIPS 2013, Jatinangor, Bandung, 7/5/13. https://doi.org/10.1063/1.4820277
@inproceedings{c69f2b0324174d7db37d3efae773a17d,
title = "Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition",
abstract = "Binderless activated carbon monolith (ACM) was prepared from pre-carbonized rubber wood sawdust (RWSD). The effect of the carbonization temperature (400, 500, 600, 700, 800 dan 900 °C) on porosity characteristic of the ACM have been studied. The optimum carbonization temperature for obtaining ACM with high surface area of 600 °C with CO2 activation at 800 °C for one hour. At this condition, the surface area as high as 733 m2 g-1 could be successfully obtained. By improved the activation temperature at 900 °C for 2.5 h, it was found that the surface area of 860 m2 g-1. For this condition, the ACM exhibit the specific capacitance of 90 F g-1. In addition the termogravimertic (TG)-differential termografimertic (DTG) and field emission scanning electron microscope (FESEM) measurement were also performed on the ACMs and the result has been studied. Finally, it was conclude that the high surface area of ACM from RWSD could be produced by proper selections of carbonization and activation condition.",
keywords = "Activated carbon, Specific capacitance, Supercapacitor",
author = "E. Taer and Mohamad Deraman and R. Taslim and Iwantono",
year = "2013",
doi = "10.1063/1.4820277",
language = "English",
isbn = "9780735411807",
volume = "1554",
pages = "33--37",
booktitle = "AIP Conference Proceedings",

}

TY - GEN

T1 - Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition

AU - Taer, E.

AU - Deraman, Mohamad

AU - Taslim, R.

AU - Iwantono,

PY - 2013

Y1 - 2013

N2 - Binderless activated carbon monolith (ACM) was prepared from pre-carbonized rubber wood sawdust (RWSD). The effect of the carbonization temperature (400, 500, 600, 700, 800 dan 900 °C) on porosity characteristic of the ACM have been studied. The optimum carbonization temperature for obtaining ACM with high surface area of 600 °C with CO2 activation at 800 °C for one hour. At this condition, the surface area as high as 733 m2 g-1 could be successfully obtained. By improved the activation temperature at 900 °C for 2.5 h, it was found that the surface area of 860 m2 g-1. For this condition, the ACM exhibit the specific capacitance of 90 F g-1. In addition the termogravimertic (TG)-differential termografimertic (DTG) and field emission scanning electron microscope (FESEM) measurement were also performed on the ACMs and the result has been studied. Finally, it was conclude that the high surface area of ACM from RWSD could be produced by proper selections of carbonization and activation condition.

AB - Binderless activated carbon monolith (ACM) was prepared from pre-carbonized rubber wood sawdust (RWSD). The effect of the carbonization temperature (400, 500, 600, 700, 800 dan 900 °C) on porosity characteristic of the ACM have been studied. The optimum carbonization temperature for obtaining ACM with high surface area of 600 °C with CO2 activation at 800 °C for one hour. At this condition, the surface area as high as 733 m2 g-1 could be successfully obtained. By improved the activation temperature at 900 °C for 2.5 h, it was found that the surface area of 860 m2 g-1. For this condition, the ACM exhibit the specific capacitance of 90 F g-1. In addition the termogravimertic (TG)-differential termografimertic (DTG) and field emission scanning electron microscope (FESEM) measurement were also performed on the ACMs and the result has been studied. Finally, it was conclude that the high surface area of ACM from RWSD could be produced by proper selections of carbonization and activation condition.

KW - Activated carbon

KW - Specific capacitance

KW - Supercapacitor

UR - http://www.scopus.com/inward/record.url?scp=84885002582&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84885002582&partnerID=8YFLogxK

U2 - 10.1063/1.4820277

DO - 10.1063/1.4820277

M3 - Conference contribution

SN - 9780735411807

VL - 1554

SP - 33

EP - 37

BT - AIP Conference Proceedings

ER -