Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal

C. L. Nur Azida, Azman Jalar @ Jalil, Norinsan Kamil Othman, A. R. Daud

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

As-welded AA6061 Al alloy using Al-Si-Mg (ER 4043) filler metal was subjected to oxidation exposure in flowing air gas for 40hrs at 600°C at a total pressure of approximately 1 atm. SEM and EDAX were chosen to characterize the morphology microstructure of oxide formation on welded joint after oxidation process. Different oxide morphology were found on parent and fusion metal due to the differences of the alloying element. The morphology of the oxide shows the protection oxide surface were developed on parent metal while non-protective oxide formed on fusion metal.

Original languageEnglish
Title of host publicationApplied Mechanics and Materials
Pages46-49
Number of pages4
Volume66-68
DOIs
Publication statusPublished - 2011
Event2011 International Conference on Mechanical Materials and Manufacturing Engineering, ICMMME 2011 - Nanchang
Duration: 20 Jun 201122 Jun 2011

Publication series

NameApplied Mechanics and Materials
Volume66-68
ISSN (Print)16609336
ISSN (Electronic)16627482

Other

Other2011 International Conference on Mechanical Materials and Manufacturing Engineering, ICMMME 2011
CityNanchang
Period20/6/1122/6/11

Fingerprint

Filler metals
Oxidation
Oxides
Fusion reactions
Metals
Alloying elements
Energy dispersive spectroscopy
Welds
Microstructure
Scanning electron microscopy
Air
Gases

Keywords

  • Aa6061 Al alloy
  • ER 4043 filler metal
  • Oxidation

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Nur Azida, C. L., Jalar @ Jalil, A., Othman, N. K., & Daud, A. R. (2011). Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal. In Applied Mechanics and Materials (Vol. 66-68, pp. 46-49). (Applied Mechanics and Materials; Vol. 66-68). https://doi.org/10.4028/www.scientific.net/AMM.66-68.46

Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal. / Nur Azida, C. L.; Jalar @ Jalil, Azman; Othman, Norinsan Kamil; Daud, A. R.

Applied Mechanics and Materials. Vol. 66-68 2011. p. 46-49 (Applied Mechanics and Materials; Vol. 66-68).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Nur Azida, CL, Jalar @ Jalil, A, Othman, NK & Daud, AR 2011, Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal. in Applied Mechanics and Materials. vol. 66-68, Applied Mechanics and Materials, vol. 66-68, pp. 46-49, 2011 International Conference on Mechanical Materials and Manufacturing Engineering, ICMMME 2011, Nanchang, 20/6/11. https://doi.org/10.4028/www.scientific.net/AMM.66-68.46
Nur Azida CL, Jalar @ Jalil A, Othman NK, Daud AR. Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal. In Applied Mechanics and Materials. Vol. 66-68. 2011. p. 46-49. (Applied Mechanics and Materials). https://doi.org/10.4028/www.scientific.net/AMM.66-68.46
Nur Azida, C. L. ; Jalar @ Jalil, Azman ; Othman, Norinsan Kamil ; Daud, A. R. / Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal. Applied Mechanics and Materials. Vol. 66-68 2011. pp. 46-49 (Applied Mechanics and Materials).
@inproceedings{07f6dbc899c74bb69a8e95c67bb4ea6a,
title = "Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal",
abstract = "As-welded AA6061 Al alloy using Al-Si-Mg (ER 4043) filler metal was subjected to oxidation exposure in flowing air gas for 40hrs at 600°C at a total pressure of approximately 1 atm. SEM and EDAX were chosen to characterize the morphology microstructure of oxide formation on welded joint after oxidation process. Different oxide morphology were found on parent and fusion metal due to the differences of the alloying element. The morphology of the oxide shows the protection oxide surface were developed on parent metal while non-protective oxide formed on fusion metal.",
keywords = "Aa6061 Al alloy, ER 4043 filler metal, Oxidation",
author = "{Nur Azida}, {C. L.} and {Jalar @ Jalil}, Azman and Othman, {Norinsan Kamil} and Daud, {A. R.}",
year = "2011",
doi = "10.4028/www.scientific.net/AMM.66-68.46",
language = "English",
isbn = "9783037851852",
volume = "66-68",
series = "Applied Mechanics and Materials",
pages = "46--49",
booktitle = "Applied Mechanics and Materials",

}

TY - GEN

T1 - Oxidation effect on welded AA6061 Al alloy using ER4043 filler metal

AU - Nur Azida, C. L.

AU - Jalar @ Jalil, Azman

AU - Othman, Norinsan Kamil

AU - Daud, A. R.

PY - 2011

Y1 - 2011

N2 - As-welded AA6061 Al alloy using Al-Si-Mg (ER 4043) filler metal was subjected to oxidation exposure in flowing air gas for 40hrs at 600°C at a total pressure of approximately 1 atm. SEM and EDAX were chosen to characterize the morphology microstructure of oxide formation on welded joint after oxidation process. Different oxide morphology were found on parent and fusion metal due to the differences of the alloying element. The morphology of the oxide shows the protection oxide surface were developed on parent metal while non-protective oxide formed on fusion metal.

AB - As-welded AA6061 Al alloy using Al-Si-Mg (ER 4043) filler metal was subjected to oxidation exposure in flowing air gas for 40hrs at 600°C at a total pressure of approximately 1 atm. SEM and EDAX were chosen to characterize the morphology microstructure of oxide formation on welded joint after oxidation process. Different oxide morphology were found on parent and fusion metal due to the differences of the alloying element. The morphology of the oxide shows the protection oxide surface were developed on parent metal while non-protective oxide formed on fusion metal.

KW - Aa6061 Al alloy

KW - ER 4043 filler metal

KW - Oxidation

UR - http://www.scopus.com/inward/record.url?scp=79961182514&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=79961182514&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/AMM.66-68.46

DO - 10.4028/www.scientific.net/AMM.66-68.46

M3 - Conference contribution

SN - 9783037851852

VL - 66-68

T3 - Applied Mechanics and Materials

SP - 46

EP - 49

BT - Applied Mechanics and Materials

ER -