Microstructure and strength of extruded porous HA ceramics.

M. Rusnah, Andanastuti Muchtar, B. Idris

Research output: Contribution to journalArticle

Abstract

The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.

Original languageEnglish
Pages (from-to)83-84
Number of pages2
JournalThe Medical journal of Malaysia
Volume59 Suppl B
Publication statusPublished - May 2004
Externally publishedYes

Fingerprint

Ceramics
Durapatite
Temperature

ASJC Scopus subject areas

  • Medicine(all)

Cite this

Microstructure and strength of extruded porous HA ceramics. / Rusnah, M.; Muchtar, Andanastuti; Idris, B.

In: The Medical journal of Malaysia, Vol. 59 Suppl B, 05.2004, p. 83-84.

Research output: Contribution to journalArticle

@article{91f709d613bf4ba88323541f0076ca89,
title = "Microstructure and strength of extruded porous HA ceramics.",
abstract = "The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.",
author = "M. Rusnah and Andanastuti Muchtar and B. Idris",
year = "2004",
month = "5",
language = "English",
volume = "59 Suppl B",
pages = "83--84",
journal = "Medical Journal of Malaysia",
issn = "0300-5283",
publisher = "Malaysian Medical Association",

}

TY - JOUR

T1 - Microstructure and strength of extruded porous HA ceramics.

AU - Rusnah, M.

AU - Muchtar, Andanastuti

AU - Idris, B.

PY - 2004/5

Y1 - 2004/5

N2 - The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.

AB - The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.

UR - http://www.scopus.com/inward/record.url?scp=16544363532&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=16544363532&partnerID=8YFLogxK

M3 - Article

C2 - 15468830

AN - SCOPUS:16544363532

VL - 59 Suppl B

SP - 83

EP - 84

JO - Medical Journal of Malaysia

JF - Medical Journal of Malaysia

SN - 0300-5283

ER -