Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite

N. N. Bonnia, Sahrim Ahmad, S. N. Surip, S. S. Nurul, H. N. Azlina, H. Anuar

Research output: Chapter in Book/Report/Conference proceedingConference contribution

7 Citations (Scopus)

Abstract

Crosslinked polyester clay nanocomposites were prepared by dispersing originically modified montmorillonite in prepromoted polyester resin and subsequently crosslinked using methyl ethyl ketone peroxide catalyst at different clay concentration. Cure process and the mechanical properties of rubber toughened polyester clay composite have been studied. Rubber toughened thermoset polyester composite were prepared by adding 3 per hundred rubber (phr) of liquid natural rubber (LNR) was used in the mixing of producing this composite. Modification of polyester matrix was done due to the brittle problem of polyester composite. Addition of LNR will increase the toughness of composite and produce ductile polyester. Two types of composites were produced which is clay-lnr polyester composite and clay polyester composite. Addition of liquid natural rubber significantly increased the impact strength and flexural properties. Result shows that addition of 6% of clay-lnr composite give good properties on impact, strength and flexural. From the ESCR test, both composites showed good resistance to environmental.

Original languageEnglish
Title of host publicationAdvanced Materials Research
Pages318-321
Number of pages4
Volume576
DOIs
Publication statusPublished - 2012
EventInternational Conference on Advances in Manufacturing and Materials Engineering, ICAMME 2012 - Kuala Lumpur
Duration: 3 Jul 20125 Jul 2012

Publication series

NameAdvanced Materials Research
Volume576
ISSN (Print)10226680

Other

OtherInternational Conference on Advances in Manufacturing and Materials Engineering, ICAMME 2012
CityKuala Lumpur
Period3/7/125/7/12

Fingerprint

Polyesters
Rubber
Clay
Mechanical properties
Composite materials
Impact strength
Liquids
Polyester resins
Thermosets
Peroxides
Clay minerals
Ketones
Toughness
Nanocomposites
Catalysts

Keywords

  • Nanoclay
  • Polyester
  • Rubber Toughened
  • Thermoset

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Bonnia, N. N., Ahmad, S., Surip, S. N., Nurul, S. S., Azlina, H. N., & Anuar, H. (2012). Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite. In Advanced Materials Research (Vol. 576, pp. 318-321). (Advanced Materials Research; Vol. 576). https://doi.org/10.4028/www.scientific.net/AMR.576.318

Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite. / Bonnia, N. N.; Ahmad, Sahrim; Surip, S. N.; Nurul, S. S.; Azlina, H. N.; Anuar, H.

Advanced Materials Research. Vol. 576 2012. p. 318-321 (Advanced Materials Research; Vol. 576).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Bonnia, NN, Ahmad, S, Surip, SN, Nurul, SS, Azlina, HN & Anuar, H 2012, Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite. in Advanced Materials Research. vol. 576, Advanced Materials Research, vol. 576, pp. 318-321, International Conference on Advances in Manufacturing and Materials Engineering, ICAMME 2012, Kuala Lumpur, 3/7/12. https://doi.org/10.4028/www.scientific.net/AMR.576.318
Bonnia NN, Ahmad S, Surip SN, Nurul SS, Azlina HN, Anuar H. Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite. In Advanced Materials Research. Vol. 576. 2012. p. 318-321. (Advanced Materials Research). https://doi.org/10.4028/www.scientific.net/AMR.576.318
Bonnia, N. N. ; Ahmad, Sahrim ; Surip, S. N. ; Nurul, S. S. ; Azlina, H. N. ; Anuar, H. / Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite. Advanced Materials Research. Vol. 576 2012. pp. 318-321 (Advanced Materials Research).
@inproceedings{59d504b77aa84991afb4678952b6a87f,
title = "Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite",
abstract = "Crosslinked polyester clay nanocomposites were prepared by dispersing originically modified montmorillonite in prepromoted polyester resin and subsequently crosslinked using methyl ethyl ketone peroxide catalyst at different clay concentration. Cure process and the mechanical properties of rubber toughened polyester clay composite have been studied. Rubber toughened thermoset polyester composite were prepared by adding 3 per hundred rubber (phr) of liquid natural rubber (LNR) was used in the mixing of producing this composite. Modification of polyester matrix was done due to the brittle problem of polyester composite. Addition of LNR will increase the toughness of composite and produce ductile polyester. Two types of composites were produced which is clay-lnr polyester composite and clay polyester composite. Addition of liquid natural rubber significantly increased the impact strength and flexural properties. Result shows that addition of 6{\%} of clay-lnr composite give good properties on impact, strength and flexural. From the ESCR test, both composites showed good resistance to environmental.",
keywords = "Nanoclay, Polyester, Rubber Toughened, Thermoset",
author = "Bonnia, {N. N.} and Sahrim Ahmad and Surip, {S. N.} and Nurul, {S. S.} and Azlina, {H. N.} and H. Anuar",
year = "2012",
doi = "10.4028/www.scientific.net/AMR.576.318",
language = "English",
isbn = "9783037854983",
volume = "576",
series = "Advanced Materials Research",
pages = "318--321",
booktitle = "Advanced Materials Research",

}

TY - GEN

T1 - Mechanical properties and environmental stress cracking resistance of rubber toughened polyester/clay composite

AU - Bonnia, N. N.

AU - Ahmad, Sahrim

AU - Surip, S. N.

AU - Nurul, S. S.

AU - Azlina, H. N.

AU - Anuar, H.

PY - 2012

Y1 - 2012

N2 - Crosslinked polyester clay nanocomposites were prepared by dispersing originically modified montmorillonite in prepromoted polyester resin and subsequently crosslinked using methyl ethyl ketone peroxide catalyst at different clay concentration. Cure process and the mechanical properties of rubber toughened polyester clay composite have been studied. Rubber toughened thermoset polyester composite were prepared by adding 3 per hundred rubber (phr) of liquid natural rubber (LNR) was used in the mixing of producing this composite. Modification of polyester matrix was done due to the brittle problem of polyester composite. Addition of LNR will increase the toughness of composite and produce ductile polyester. Two types of composites were produced which is clay-lnr polyester composite and clay polyester composite. Addition of liquid natural rubber significantly increased the impact strength and flexural properties. Result shows that addition of 6% of clay-lnr composite give good properties on impact, strength and flexural. From the ESCR test, both composites showed good resistance to environmental.

AB - Crosslinked polyester clay nanocomposites were prepared by dispersing originically modified montmorillonite in prepromoted polyester resin and subsequently crosslinked using methyl ethyl ketone peroxide catalyst at different clay concentration. Cure process and the mechanical properties of rubber toughened polyester clay composite have been studied. Rubber toughened thermoset polyester composite were prepared by adding 3 per hundred rubber (phr) of liquid natural rubber (LNR) was used in the mixing of producing this composite. Modification of polyester matrix was done due to the brittle problem of polyester composite. Addition of LNR will increase the toughness of composite and produce ductile polyester. Two types of composites were produced which is clay-lnr polyester composite and clay polyester composite. Addition of liquid natural rubber significantly increased the impact strength and flexural properties. Result shows that addition of 6% of clay-lnr composite give good properties on impact, strength and flexural. From the ESCR test, both composites showed good resistance to environmental.

KW - Nanoclay

KW - Polyester

KW - Rubber Toughened

KW - Thermoset

UR - http://www.scopus.com/inward/record.url?scp=84869401622&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84869401622&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/AMR.576.318

DO - 10.4028/www.scientific.net/AMR.576.318

M3 - Conference contribution

AN - SCOPUS:84869401622

SN - 9783037854983

VL - 576

T3 - Advanced Materials Research

SP - 318

EP - 321

BT - Advanced Materials Research

ER -