Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate

Farah Atiqah Abdul Azam, Hamisah Ismail, Roslinda Shamsudin, Zalita Zainuddin, Muhammad Azmi Abdul Hamid

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The morphology and surface topography of calcium silicate coated on Ti6Al4V implant were studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction analysis (XRD) respectively. The surface of titanium alloy plates was mechanically ground with 320, 800 and 1200 grits of SiC abrasive paper followed by surface polishing into mirror-like finish. The synthesized β-CaSiO3 was deposited onto the Ti6Al4V substrate using electron beam evaporator. After coating, calcium silicate was heat treated at 500 °C for 1 hour. Characterization of the calcium silicate coated on Ti6Al4V substrate using e-beam evaporation technique demonstrated that 5 wt% of PVA addition was able to improve the coating-to-substrate adhesion.

Original languageEnglish
Title of host publicationCurrent Trends in Materials Engineering
PublisherTrans Tech Publications Ltd
Pages83-87
Number of pages5
Volume694
ISBN (Print)9783035710199
DOIs
Publication statusPublished - 2016
Event24th Scientific Conference of the Microscopy Society Malaysia, SCMSM 2015 - Malacca, Malaysia
Duration: 2 Dec 20154 Dec 2015

Publication series

NameKey Engineering Materials
Volume694
ISSN (Print)10139826

Other

Other24th Scientific Conference of the Microscopy Society Malaysia, SCMSM 2015
CountryMalaysia
CityMalacca
Period2/12/154/12/15

Fingerprint

Calcium silicate
Adhesion
Coatings
Substrates
Surface topography
Evaporators
Polishing
Titanium alloys
Abrasives
Field emission
X ray diffraction analysis
Electron beams
Evaporation
Mirrors
Scanning electron microscopy
titanium alloy (TiAl6V4)
calcium silicate

Keywords

  • Calcium silicate
  • Electron beam deposition
  • Ti-6Al-4V alloy

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Abdul Azam, F. A., Ismail, H., Shamsudin, R., Zainuddin, Z., & Abdul Hamid, M. A. (2016). Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate. In Current Trends in Materials Engineering (Vol. 694, pp. 83-87). (Key Engineering Materials; Vol. 694). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.694.83

Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate. / Abdul Azam, Farah Atiqah; Ismail, Hamisah; Shamsudin, Roslinda; Zainuddin, Zalita; Abdul Hamid, Muhammad Azmi.

Current Trends in Materials Engineering. Vol. 694 Trans Tech Publications Ltd, 2016. p. 83-87 (Key Engineering Materials; Vol. 694).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abdul Azam, FA, Ismail, H, Shamsudin, R, Zainuddin, Z & Abdul Hamid, MA 2016, Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate. in Current Trends in Materials Engineering. vol. 694, Key Engineering Materials, vol. 694, Trans Tech Publications Ltd, pp. 83-87, 24th Scientific Conference of the Microscopy Society Malaysia, SCMSM 2015, Malacca, Malaysia, 2/12/15. https://doi.org/10.4028/www.scientific.net/KEM.694.83
Abdul Azam FA, Ismail H, Shamsudin R, Zainuddin Z, Abdul Hamid MA. Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate. In Current Trends in Materials Engineering. Vol. 694. Trans Tech Publications Ltd. 2016. p. 83-87. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.694.83
Abdul Azam, Farah Atiqah ; Ismail, Hamisah ; Shamsudin, Roslinda ; Zainuddin, Zalita ; Abdul Hamid, Muhammad Azmi. / Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate. Current Trends in Materials Engineering. Vol. 694 Trans Tech Publications Ltd, 2016. pp. 83-87 (Key Engineering Materials).
@inproceedings{7c85965e90cf4154a85824ab0fa86dea,
title = "Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate",
abstract = "The morphology and surface topography of calcium silicate coated on Ti6Al4V implant were studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction analysis (XRD) respectively. The surface of titanium alloy plates was mechanically ground with 320, 800 and 1200 grits of SiC abrasive paper followed by surface polishing into mirror-like finish. The synthesized β-CaSiO3 was deposited onto the Ti6Al4V substrate using electron beam evaporator. After coating, calcium silicate was heat treated at 500 °C for 1 hour. Characterization of the calcium silicate coated on Ti6Al4V substrate using e-beam evaporation technique demonstrated that 5 wt{\%} of PVA addition was able to improve the coating-to-substrate adhesion.",
keywords = "Calcium silicate, Electron beam deposition, Ti-6Al-4V alloy",
author = "{Abdul Azam}, {Farah Atiqah} and Hamisah Ismail and Roslinda Shamsudin and Zalita Zainuddin and {Abdul Hamid}, {Muhammad Azmi}",
year = "2016",
doi = "10.4028/www.scientific.net/KEM.694.83",
language = "English",
isbn = "9783035710199",
volume = "694",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "83--87",
booktitle = "Current Trends in Materials Engineering",

}

TY - GEN

T1 - Characterizations on morphology and adhesion of calcium silicate coating on Ti6Al4V substrate

AU - Abdul Azam, Farah Atiqah

AU - Ismail, Hamisah

AU - Shamsudin, Roslinda

AU - Zainuddin, Zalita

AU - Abdul Hamid, Muhammad Azmi

PY - 2016

Y1 - 2016

N2 - The morphology and surface topography of calcium silicate coated on Ti6Al4V implant were studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction analysis (XRD) respectively. The surface of titanium alloy plates was mechanically ground with 320, 800 and 1200 grits of SiC abrasive paper followed by surface polishing into mirror-like finish. The synthesized β-CaSiO3 was deposited onto the Ti6Al4V substrate using electron beam evaporator. After coating, calcium silicate was heat treated at 500 °C for 1 hour. Characterization of the calcium silicate coated on Ti6Al4V substrate using e-beam evaporation technique demonstrated that 5 wt% of PVA addition was able to improve the coating-to-substrate adhesion.

AB - The morphology and surface topography of calcium silicate coated on Ti6Al4V implant were studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction analysis (XRD) respectively. The surface of titanium alloy plates was mechanically ground with 320, 800 and 1200 grits of SiC abrasive paper followed by surface polishing into mirror-like finish. The synthesized β-CaSiO3 was deposited onto the Ti6Al4V substrate using electron beam evaporator. After coating, calcium silicate was heat treated at 500 °C for 1 hour. Characterization of the calcium silicate coated on Ti6Al4V substrate using e-beam evaporation technique demonstrated that 5 wt% of PVA addition was able to improve the coating-to-substrate adhesion.

KW - Calcium silicate

KW - Electron beam deposition

KW - Ti-6Al-4V alloy

UR - http://www.scopus.com/inward/record.url?scp=84974717999&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84974717999&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.694.83

DO - 10.4028/www.scientific.net/KEM.694.83

M3 - Conference contribution

AN - SCOPUS:84974717999

SN - 9783035710199

VL - 694

T3 - Key Engineering Materials

SP - 83

EP - 87

BT - Current Trends in Materials Engineering

PB - Trans Tech Publications Ltd

ER -