Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

Titanium dioxide had been noticed thoroughly for their superiorities over conventional p-n junction devices, such as low cost and slighter toxic in construction. In this research, we present and study the preparation of Carbon Nanotube/TiO 2 acid treatment nanocomposite by the alteration of acid-catalyzed sol-gel method. The CNT/TiO 2 nanocomposite powder was acid treatment in NaOH solution and directed on FTO glass substrates. The CNT/TiO 2 paste was doctor blade onto the substrate plate to form a 1.0 cm 2 active region and later on annealed at 550°C, 650°C and 750°C for 30 min. The characterization of the TiO 2 adhesive was carried out by X-ray diffraction (XRD) and the results indicate that the particles of CNT/TiO 2 are in rutile form not in anatase structure. The micrographs of scanning electron microscopy (SEM) images prove that the thin film pastes have high porosity and the Brunauer Emmett Teller (BET) result show the surface area, pore volume and pore size for the CNT/TiO 2 thin film.

Original languageEnglish
Title of host publication2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts
Pages291-294
Number of pages4
DOIs
Publication statusPublished - 2011
Event2011 IEEE Regional Symposium on Micro and Nano Electronics, RSM 2011 - Kota Kinabalu, Sabah
Duration: 28 Sep 201130 Sep 2011

Other

Other2011 IEEE Regional Symposium on Micro and Nano Electronics, RSM 2011
CityKota Kinabalu, Sabah
Period28/9/1130/9/11

Fingerprint

Titanium dioxide
Sol-gel process
Carbon nanotubes
Nanocomposites
Acids
Thin films
Substrates
Pore size
Adhesives
Porosity
Powders
X ray diffraction
Glass
Scanning electron microscopy
Costs

ASJC Scopus subject areas

  • Electrical and Electronic Engineering

Cite this

Razali, M. Z., Abdullah, H., Taha, M. R., & Jit Singh, M. S. (2011). Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method. In 2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts (pp. 291-294). [6088346] https://doi.org/10.1109/RSM.2011.6088346

Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method. / Razali, M. Z.; Abdullah, Huda; Taha, Mohd. Raihan; Jit Singh, Mandeep Singh.

2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts. 2011. p. 291-294 6088346.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Razali, MZ, Abdullah, H, Taha, MR & Jit Singh, MS 2011, Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method. in 2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts., 6088346, pp. 291-294, 2011 IEEE Regional Symposium on Micro and Nano Electronics, RSM 2011, Kota Kinabalu, Sabah, 28/9/11. https://doi.org/10.1109/RSM.2011.6088346
Razali MZ, Abdullah H, Taha MR, Jit Singh MS. Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method. In 2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts. 2011. p. 291-294. 6088346 https://doi.org/10.1109/RSM.2011.6088346
Razali, M. Z. ; Abdullah, Huda ; Taha, Mohd. Raihan ; Jit Singh, Mandeep Singh. / Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method. 2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts. 2011. pp. 291-294
@inproceedings{5c39b6e56f704af299d0ff3817351bac,
title = "Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method",
abstract = "Titanium dioxide had been noticed thoroughly for their superiorities over conventional p-n junction devices, such as low cost and slighter toxic in construction. In this research, we present and study the preparation of Carbon Nanotube/TiO 2 acid treatment nanocomposite by the alteration of acid-catalyzed sol-gel method. The CNT/TiO 2 nanocomposite powder was acid treatment in NaOH solution and directed on FTO glass substrates. The CNT/TiO 2 paste was doctor blade onto the substrate plate to form a 1.0 cm 2 active region and later on annealed at 550°C, 650°C and 750°C for 30 min. The characterization of the TiO 2 adhesive was carried out by X-ray diffraction (XRD) and the results indicate that the particles of CNT/TiO 2 are in rutile form not in anatase structure. The micrographs of scanning electron microscopy (SEM) images prove that the thin film pastes have high porosity and the Brunauer Emmett Teller (BET) result show the surface area, pore volume and pore size for the CNT/TiO 2 thin film.",
author = "Razali, {M. Z.} and Huda Abdullah and Taha, {Mohd. Raihan} and {Jit Singh}, {Mandeep Singh}",
year = "2011",
doi = "10.1109/RSM.2011.6088346",
language = "English",
isbn = "9781612848464",
pages = "291--294",
booktitle = "2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts",

}

TY - GEN

T1 - Characterization of carbon nanotube/titanium dioxide acid treatment nanocomposite structure using sol-gel method

AU - Razali, M. Z.

AU - Abdullah, Huda

AU - Taha, Mohd. Raihan

AU - Jit Singh, Mandeep Singh

PY - 2011

Y1 - 2011

N2 - Titanium dioxide had been noticed thoroughly for their superiorities over conventional p-n junction devices, such as low cost and slighter toxic in construction. In this research, we present and study the preparation of Carbon Nanotube/TiO 2 acid treatment nanocomposite by the alteration of acid-catalyzed sol-gel method. The CNT/TiO 2 nanocomposite powder was acid treatment in NaOH solution and directed on FTO glass substrates. The CNT/TiO 2 paste was doctor blade onto the substrate plate to form a 1.0 cm 2 active region and later on annealed at 550°C, 650°C and 750°C for 30 min. The characterization of the TiO 2 adhesive was carried out by X-ray diffraction (XRD) and the results indicate that the particles of CNT/TiO 2 are in rutile form not in anatase structure. The micrographs of scanning electron microscopy (SEM) images prove that the thin film pastes have high porosity and the Brunauer Emmett Teller (BET) result show the surface area, pore volume and pore size for the CNT/TiO 2 thin film.

AB - Titanium dioxide had been noticed thoroughly for their superiorities over conventional p-n junction devices, such as low cost and slighter toxic in construction. In this research, we present and study the preparation of Carbon Nanotube/TiO 2 acid treatment nanocomposite by the alteration of acid-catalyzed sol-gel method. The CNT/TiO 2 nanocomposite powder was acid treatment in NaOH solution and directed on FTO glass substrates. The CNT/TiO 2 paste was doctor blade onto the substrate plate to form a 1.0 cm 2 active region and later on annealed at 550°C, 650°C and 750°C for 30 min. The characterization of the TiO 2 adhesive was carried out by X-ray diffraction (XRD) and the results indicate that the particles of CNT/TiO 2 are in rutile form not in anatase structure. The micrographs of scanning electron microscopy (SEM) images prove that the thin film pastes have high porosity and the Brunauer Emmett Teller (BET) result show the surface area, pore volume and pore size for the CNT/TiO 2 thin film.

UR - http://www.scopus.com/inward/record.url?scp=83755194808&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=83755194808&partnerID=8YFLogxK

U2 - 10.1109/RSM.2011.6088346

DO - 10.1109/RSM.2011.6088346

M3 - Conference contribution

SN - 9781612848464

SP - 291

EP - 294

BT - 2011 IEEE Regional Symposium on Micro and Nanoelectronics, RSM 2011 - Programme and Abstracts

ER -